1.10CrMoAl鋼板的中文讀音為一零鉻鉬鋁。
2.10CrMoAl鋼板標準:舞技
3.10CrMoAl鋼板的尺寸、形狀、重量和允許偏差:應符合GB/T709-1988的規(guī)定。
4. Heat treatment status of 10CrMoAl steel plate: hot rolling, control and binding, normalizing, tempering, annealing and quenching, etc
1) Normalizing: cool the steel plate to the appropriate temperature in the air
2) Tempering: Heat the steel plate at a certain appropriate temperature for a long time before cooling
3) Annealing: It means that the steel plate is heated to an appropriate temperature and cooled slowly according to the heating time of different materials and specifications
4) Quenching: It refers to rapid cooling of steel plates in water, oil or other medium without adding salt after heating and holding heat
五、10CrMoAl是一種耐海水腐蝕的專用鋼材。10CrMoAl材料，是沿海電廠，沿海油田，沿海天然氣及石化廠輸送水，油氣及含海水介質(zhì)的最理想的管路及加工件制作材料。還可用于制做閥門的法蘭盤。
10CrMoAL密度：7.85 t/m3
10CrMoAl材料，是沿海電廠，沿海油田，沿海天然氣及石化廠輸送水，油氣及含海水介質(zhì)的最理想的管路及加工件制作材料。
10CrMoAL能耐腐蝕的原因：
1、10CrMoAl材料中的Al（鋁），能與空氣中的O（氧）化學反應生成Al2O3（三氧化二鋁）.從而行成保護膜，既防腐又耐腐。
2、10CrMoAl中的Cr(鉻），Mo（鉬），離子在海水中能自動補充Cl（氯）離子對鋼材點腐蝕形成的空隙，開成致密保護層，阻止點腐蝕向縱深發(fā)展。進而起到耐腐，使使用壽命加長。
10CrMoAl材料中的Al（鋁），能與空氣中的O（氧）化學反應生成Al2O3（三氧化二鋁）.從而行成保護膜，既防腐又耐腐。10CrMoAl中的Cr(鉻），Mo（鉬），離子在海水中能自動補充Cl（氯）離子對鋼材點腐蝕形成的空隙，開成致密保護層，阻止點腐蝕向縱深發(fā)展。使鋼板使用壽命加長10CrMoAl材料焊接性能比較好，配有專用耐腐焊條“海O3”，無特殊焊接要求。
七、10CrMoAl密度為7.85 t/m
八、10CrMoAl鋼板化學成分：
10CrMoAl合金結構鋼板化學成分%
C
Mn
Ni
Si
P
0.12
0.35-0.65
0.03
0.2-0.5
0.025
S
Cr
Cu
Mo
AL
0.025
0.8-1.2
0.03
0.2-0.35
0.4-0.8
九、10CrMoAl鋼板力學性能：
牌號
抗拉強度(MPa)
屈服強度(MPa)
伸長率(%)
10CrMoAl
≥490
≥323
≥17
抗拉強度（MPa）≥490
屈服強度（MPa）≥323
伸長率（%）≥17
（金屬材料的屈服強度應低于抗拉強度。）
十、10CrMoA1鋼板技術條件
技術要求：鋼的牌號及化學成分階段(熔煉分析，%)應符合規(guī)定。
十一、10CrMoAl鋼板用途：
這個上文也提到過，它主要用來制作管道及設備，具有很強的耐腐蝕性，安裝也很方便等優(yōu)點，并大大節(jié)約了成本。一種耐海水腐蝕的專用鋼材，所以他在沿海電廠，沿海油田，沿海天然氣及石化廠輸送水，油氣及含海水介質(zhì)的管路中被廣泛運用，此外還用于制做閥門的法蘭。